I did verify my model and it seems correct, may I know why there is a difference between the obtained flow stress strain curve vs the material database flow stress strain curve?
Also why are the curves different in global and individual ones in the database. the global shows a peak flow stress of close to 250 Mpa but not same in the individual table?
Please find the below plot of flow stress vs strain after doing the test in Simufact forging module, dies with no heat conduction and applied boundary conditions.
could you please confirm if my model is correct, or if am doing any mistakes please correct me .
I did verify my model and it seems correct, may I know why there is a difference between the obtained flow stress strain curve vs the material database flow stress strain curve?
Also why are the curves different in global and individual ones in the database. the global shows a peak flow stress of close to 250 Mpa but not same in the individual table?
Please find the below plot of flow stress vs strain after doing the test in Simufact forging module, dies with no heat conduction and applied boundary conditions.
could you please confirm if my model is correct, or if am doing any mistakes please correct me .